Iscar 10pc Carbide Insert WNMG3-1-GN IC20 WNMG 06T304-GN ISO Grad M10-M25 K10-K20
Turning carbide Insert Uncoated
: WNMG-GN Double-sided trigon insert, secure cutting edge, for medium- and semi-roughing on steel and cast iron.
Inch carbide insert dimension
| L | IC | S | RE | ft (min) |
ft (max) |
ap (min) |
ap (max) |
|---|---|---|---|---|---|---|---|
| .257 | .375 | .156 | .0157 | .0055 | .0157 | .039 | .138 |
Metric Carbide Insert Dimension
| L | IC | S | RE | ft (min) |
ft (max) |
ap (min) |
ap (max) |
|---|---|---|---|---|---|---|---|
| 6.52 | 9.52 | 3.97 | 0.40 | 0.14 | 0.40 | 1.00 | 3.50 |
Used for semi finishing, finishing and semi roughing of aluminum, cast iron and stainless steel. An uncoated carbide grade.
Grade : IC20
Used for semi finishing, finishing and semi roughing of aluminum, cast iron and stainless steel. An uncoated carbide grade.
| ISO Range – P/M/K | (M10-M25)(K10-K20) |
| ISO Range – N/S/H | (H05-H15)(S05-S20)(N05-N25) |
| Grade or Coating Type | Uncoated |
| Coating Layers | Uncoated |
Cutting Speed for: WNMG 06T304-GN IC20 – 5503794
| ISO | Material | Material Designation | Material Condition | Hardness | Cutting Speed Recommendations (Vc) |
|---|---|---|---|---|---|
| N | 21 | Aluminum-wrought alloys | Not hardenable | 60 HB | 1000-2500 m/min |
| N | 22 | Aluminum-wrought alloys | Hardenable | 100 HB | 300-1000 m/min |
| N | 23 | Aluminum-cast alloys <=12% Si | Not hardenable | 75 HB | 300-1000 m/min |
| N | 24 | Aluminum-cast alloys <=12% Si | Hardenable | 90 HB | 200-600 m/min |
| N | 26 | Copper alloys >1% Pb | Free cutting | 110 HB | 250-600 m/min |
| N | 27 | Copper alloys | Brass | 90 HB | 180-400 m/min |
| N | 28 | Copper alloys | Electrolytic copper | 100 HB | 150-300 m/min |
| S | 31 | High temp. alloys Fe based | Annealed | 200 HB | 35-45 m/min |
| S | 32 | High temp. alloys Fe based | Hardened | 280 HB | 25-35 m/min |
| S | 33 | High temp. alloys Ni or Co based | Annealed | 250 HB | 25-30 m/min |
| S | 34 | High temp. alloys. Ni or Co based | Hardened | 350 HB | 20-30 m/min |
| S | 35 | High temp. alloys. Ni or Co based | Cast | 320 HB | 25-35 m/min |
| S | 36 | Titanium (pure) | Pure | 190 HB | 120-160 m/min |
| S | 37 | Titanium alloys | Alpha+beta alloys, hardened | 310 HB | 50-60 m/min |